Home > Products > Other Digital Photo Frame > Nanocrystalline Alloy Strip as Transformer Material

Nanocrystalline Alloy Strip as Transformer Material

Product Description

Product Type: Strip Carbon Content: Low Carbon Brand: Ualloy Trademark: Ualloy Material: Fesib Product Name: Nanocrystalline Alloy Strip as Transformer Materia Application: as Transformer Material Origin: Hangzhou, China Nanocrystalline Alloy Strip as transformer material 

 Application area:
l Switch power transformer and Pulse transformer iron core
l Power transformer , precision current mutual inductor iron core
l Leakage protection switch mutual inductor iron core
l Filtering inductance, storage inductance, the electric reactor iron core
l EMC common mode inductance and differential mode inductance iron core
l Saturable reactor, magnetic amplifier, Spike killer, Pulse Compressor iron core and magnetic bead
l High Saturation magnetic induction - reduce transformer volume
l High magnetic permeability low coercive force- improve transformer efficiency, mutual inductor sensitivity, reduce coil distribution parameters
l Low loss- reduce transformer temperature rise
l Good temperature stability -  under 130ºC for long-term work
l Lower price -  has the best cost performance of all the metal soft magnetic material
Typical Properties
Physical properties of Nanocrystalline alloy
Saturation magnetic induction (Bs) 1.25T Hardness (Hv) 880
Curie temperature (TC) 560ºC Density (d) 7.2g/cm3
Crystallizing temperature( Tx) 510ºC Resistivity(r) 90mW-cm
Saturation magnetostriction coefficient  (ls) <2×10-6 Continuous operating temperature range -55-130ºC
Magnetic properties of Nanocrystalline alloy
Product Type Transverse magnetic annealing No magnetic annealing  Longitudinal magnetic annealing
Initial permeability >2×104 >8×104 >1×104
Maximum permeability >5×104 >45×104 >50×104
Residual magnetic induction <0.2 T 0.6 T >0.85 T
Coercive force <1.8A/m <0.8A/m <1.8A/m
Iron loss P(20kHz, 0.5T) <30W/kg <50 W/kg <90W/kg
Iron loss P(100kHz, 0.3T) <150W/kg <150 W/kg <300W/kg
Iron loss rate(-55°C -125C ) <15% <15% <15%
The comparison between Nanocrystalline alloy and Permalloy iron alloy
Basic parameter Superfine crystal iron core Permalloy iron alloy (1J85) Ferrite
Saturation magnetic induction  Bs(T) 1.25 0.75 0.5
Residual magnetic induction Br(T) 0.2~0.9 - 0.20
Saturation magnetostriction coefficient (×10-6) <2 <2 4
Resistivity (mmW-cm ) 80 56 106
Curie temperature ºC 570 400 <200
Initial permeability μ0(Gs/Oe) >8×104 >8×104 -
Maximum permeability μm(Gs/Oe) >50×104 60×104 4×104
Coercive force Hc (A/m) <2 <1 6
Iron loss (20KHz,0.5T) (W/Kg) <35 - No
Iron loss (50KHz,0.3T) (W/Kg) <50 - No

Contact us if you need more details on Nanocrystalline Alloy. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Nanocrystalline Alloy Stirp、Nanocrystalline. If these products fail to match your need, please contact us and we would like to provide relevant information.